Oxygen level and particle size effects on sintering of binder jetting copper parts Bağlayıcı püskürtmeli eklemeli imalat yönteminde bakır parçaların sinterlenmesinde tane boyutunun ve oksijen seviyesinin etkisi

ABSTRACTCopper is one of the most conductive metallic materials. For most metals, additive manufacturing is prone to laser or electron beam powder bed fusion processes. Due to copper's high reflectivity and very high thermal conductivity, it is difficult to print 3D parts with powder bed fusion methods. Binder jetting, which is a developing 3D printing technology, has a high potential for use in order to eliminate these problems of copper and low processing costs. In this study, the effect of particle size distributionand oxygen level of the copper powders on part density, tensile strength, surface roughness and electrical properties of the final parts were investigated.ÖZETBakır en iletken metalik malzemelerden biridir. Çoğu metal için, eklemeli imalat, lazer veya elektron ışını toz yatağı füzyon işlemlerine eğilimlidir. Bakırın yüksek yansıtma özelliği ve çok yüksek ısı iletkenliği nedeniyle toz yatak füzyon yöntemleriyle 3 boyutlu parçaların basılması zordur. Bağlayıcı püskürtmeli eklemeli imalat yöntemi ile bakırın bu problemlerini ortadan kaldırmak için kullanım potansiyeli yüksek olup, düşük işleme maliyetleri gibi avantajları ile öne çıkmaktadır. Bu çalışmada, bakır tozlarının partikül boyutu dağılımının ve oksijen seviyesinin, nihai parçaların parça yoğunluğu, çekme mukavemeti, yüzey pürüzlülüğü ve elektriksel özellikleri üzerindeki etkisi araştırılmıştır.