The effect of local heating on the weld line formation in plastic ınjection molding of acrylonitrile butadiene styrene and glass fiber reinforced polypropylene Akrilonitril bütadien stiren ve cam elyaf takviyeli polipropilenin plastik enjeksiyon kalıplamasında lokal ısıtmanın birleşme izi oluşumuna etkisi

ABSTRACTIn this study, the effect of local heating on the weld line formation in a plastic injection mold was studied by using acrylonitrile butadiene styrene (ABS) and polypropylene 20 glass fiber (PP GF20) plastic material. An aluminum 6000 insert was fitted into the injection mold to set temperatures for local heating. The three parameters with three levels were selected for injection molding process parameters as insert temperature, mold temperature, and melt temperature and to produce mechanical tests specimens with weld lines and non-weld lines. L9 orthogonal array was arranged for the Taguchi method.To verify the mold design, plastic injection molding simulation software Moldex3D was implemented for plastic filling analysis. The tensile and bending test results for specimens were analyzed by using the statistics package Minitab 19.1.ÖZETBu çalışmada, plastik enjeksiyon kalıbında lokal ısıtmanın birleşme izi oluşumu üzerindeki etkisini akrilonitril bütadien stiren (ABS) ve polipropilen 20 cam elyaf (PP GF20) plastik malzemesi kullanılarak incelenmiştir. Yerel ısıtma için sıcaklıkları ayarlamak üzere enjeksiyon kalıbına bir alüminyum 6000 serisi insert parçası yerleştirildi. Enjeksiyon kalıplama proses parametreleri için insert sıcaklığı, kalıp sıcaklığı ve eriyik sıcaklığı olarak üç seviyeli üç parametre seçildi ve birleşme izi ve birleşme izi olmayan mekanik test numuneleri üretildi. Taguchi yöntemi için L9 ortogonal dizisi düzenlenmiştir.Kalıp tasarımını doğrulamak için, plastik enjeksiyon kalıplama simülasyon yazılımı Moldex3D programında plastik dolum analizi uygulanmıştır. Numuneler için çekme ve eğilme test sonuçları Minitab 19.1 istatistik programı kullanılarak analiz edildi.

Erişime Açık
Görüntülenme
24
24.10.2022 tarihinden bu yana
İndirme
1
24.10.2022 tarihinden bu yana
Son Erişim Tarihi
13 Haziran 2024 11:17
Google Kontrol
Tıklayınız
Tam Metin
Tam Metin İndirmek için tıklayın Ön izleme
Detaylı Görünüm
Eser Adı
(dc.title)
The effect of local heating on the weld line formation in plastic ınjection molding of acrylonitrile butadiene styrene and glass fiber reinforced polypropylene Akrilonitril bütadien stiren ve cam elyaf takviyeli polipropilenin plastik enjeksiyon kalıplamasında lokal ısıtmanın birleşme izi oluşumuna etkisi
Eser Sahibi
(dc.contributor.author)
Güler, Muhsin Deniz
Tez Danışmanı
(dc.contributor.advisor)
Aydın Ülker
Yayıncı
(dc.publisher)
Graduate School of Natural and Applied Sciences
Tür
(dc.type)
Yüksek Lisans
Açıklama
(dc.description)
xix, 116 pages
Açıklama
(dc.description)
29 cm. 1 CD
Özet
(dc.description.abstract)
ABSTRACTIn this study, the effect of local heating on the weld line formation in a plastic injection mold was studied by using acrylonitrile butadiene styrene (ABS) and polypropylene 20 glass fiber (PP GF20) plastic material. An aluminum 6000 insert was fitted into the injection mold to set temperatures for local heating. The three parameters with three levels were selected for injection molding process parameters as insert temperature, mold temperature, and melt temperature and to produce mechanical tests specimens with weld lines and non-weld lines. L9 orthogonal array was arranged for the Taguchi method.To verify the mold design, plastic injection molding simulation software Moldex3D was implemented for plastic filling analysis. The tensile and bending test results for specimens were analyzed by using the statistics package Minitab 19.1.ÖZETBu çalışmada, plastik enjeksiyon kalıbında lokal ısıtmanın birleşme izi oluşumu üzerindeki etkisini akrilonitril bütadien stiren (ABS) ve polipropilen 20 cam elyaf (PP GF20) plastik malzemesi kullanılarak incelenmiştir. Yerel ısıtma için sıcaklıkları ayarlamak üzere enjeksiyon kalıbına bir alüminyum 6000 serisi insert parçası yerleştirildi. Enjeksiyon kalıplama proses parametreleri için insert sıcaklığı, kalıp sıcaklığı ve eriyik sıcaklığı olarak üç seviyeli üç parametre seçildi ve birleşme izi ve birleşme izi olmayan mekanik test numuneleri üretildi. Taguchi yöntemi için L9 ortogonal dizisi düzenlenmiştir.Kalıp tasarımını doğrulamak için, plastik enjeksiyon kalıplama simülasyon yazılımı Moldex3D programında plastik dolum analizi uygulanmıştır. Numuneler için çekme ve eğilme test sonuçları Minitab 19.1 istatistik programı kullanılarak analiz edildi.
Kayıt Giriş Tarihi
(dc.date.accessioned)
04.11.2022
Açık Erişim Tarihi
(dc.date.available)
2022-11-04
Yayın Tarihi
(dc.date.issued)
2022
Yayın Dili
(dc.language.iso)
eng
Konu Başlıkları
(dc.subject)
Plastik enjeksiyon
Konu Başlıkları
(dc.subject)
Plastik - Kalıplama
Tek Biçim Adres
(dc.identifier.uri)
https://hdl.handle.net/11469/3129
Analizler
Yayın Görüntülenme
Yayın Görüntülenme
Erişilen ülkeler
Erişilen şehirler
6698 sayılı Kişisel Verilerin Korunması Kanunu kapsamında yükümlülüklerimiz ve çerez politikamız hakkında bilgi sahibi olmak için alttaki bağlantıyı kullanabilirsiniz.

creativecommons
Bu site altında yer alan tüm kaynaklar Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır.
Platforms