Surface modification of micronized quartz powders and investigation of additives as filling material in polymer matrix composite materials Mikronize kuvars tozlarının yüzey modifikasyonunun yapılması ve polimer matrisli kompozit malzemelerde dolgu malzemesi olarak incelenmesi

Akyüz, Orhan

Doktora Tezi | 2020 | Graduate School of Natural and Applied Sciences

SUMMARYThe interfacing compatibility of the matrix material with the filler material in composite materials is one of the most important factors affecting the performance of the composite. A wide variety of chemical methods are applied to increase the interfacial compatibility of the matrix material with the filler material. The most important of all is the surface modification technique, in which surface-active agents are used to reinforce the matrix-filler bond and where a chemical process is applied to the surface of the filler material.This technique is based on the chemical treatment of the filler material with surface active a . . .gents to increase the compatibility of the matrix-filler materials by forming chemical bond(s) between the matrix material and the filler as well as a physical strength in their interactions. In this study, micronized quartz (MQ) powders, in order to be used as filling material, were first modified with four different surface modification agents. Then, micronized quartz, commercially available as silanized quartz (SQ) and surface modified micronized quartz powders were mixed with Polypropylene (PP) being used as matrix material by high-speed thermokinetic mixer in order to produce composite materials.ÖZETKompozit malzemelerin performansına etki eden en önemli etkenlerden birisi, dolgu ve matris malzemelerinin arayüzey uyumudur. Her iki malzemenin arayüzey uyumunu artırmak için çeşitli kimyasal yöntemler uygulanmaktadır. Bunların en başında matris-dolgu malzemesi bağını/etkileşimini güçlendirmek için yüzey aktif ajanların kullanıldığı ve dolgu malzemesinin yüzeyine kimyasal bir işlemin uygulandığı yüzey modifikasyon tekniğidir. Bu tekniğin temeli, yüzey aktif ajanlarla kimyasal işleme tabi tutulan dolgu malzemesi ile matris malzemesi arasında fiziksel bir bağ kuvvetinin yanında kimyasal bağ oluşturularak matris-dolgu malzemesi uyumunun artırılmasına dayanmaktadır. Bu çalışmada ilk olarak dolgu malzemesi olarak kullanılan mikronize kuvars (MQ) tozları, 4 farklı yüzey modifikasyon ajanı ile muamele edilerek yüzey modifikasyon işlemi yapılmıştır. Daha sonra mikronize kuvars, ticari olarak temin edilen silanize kuvars (SQ) ve yüzey modifikasyonu yapılmış mikronize kuvars tozları ve matris malzemesi (Polipropilen, PP) birlikte yüksek hızlı termokinetik karıştırıcı ile karıştırılarak kompozit malzeme üretimleri gerçekleştirilmiştir Daha fazlası Daha az

Hybrid surface modification for fiber reinforced EPDM composites Elyaf takviyeli EPDM kompozitler için hibrit yüzey modifikasyonu

Bakiler, Gökçe

Doktora Tezi | 2021 | Graduate School of Natural and Applied Sciences

ÖZETEPDM, iyi ozon ve hava dayanımı, idare eder sıcaklık dayanımı, su ve antifriz gibi polar sıvılara olan dayanımı ve hidrokarbonlara olan zayıf dayanımı ile iyi bilinen geleneksel bir kauçuk tipidir. Bu çalışmada kullanılan elyaf tipleri karbon, basalt, PA2 cam, PP4 cam ve aramiddir. Karbon elyaf yüksek çekme mukavemeti, yüksek elastik modülüs, yüksek kırılganlık, düşük sürünme eğilimi, kimyasal inert davranış, düşük ısı genleşmesi ve iyi elektriksel iletkenlik özellikleri ile bilinmektedir. Bazalt elyaf çok yüksek sıcaklığa dayanabilir ve yangın engelleme elementi olarak davranabilir. İyi termal dayanıma, kuvvete, yüksek sürtünme . . . katsayısına ve düşük yırtılma hızına sahiptir. Deniz suyu ve UV radyasyon dayanımı yüksektir. Cam elyaflar düşük uzamada yüksek çekme mukavemetine ve düşük yoğunluğa sahiptirler. Aramid elyaflar sıcaklık dayanımı olan güçlü sentetik elyaf grubundalardır. Elyaflar daha yüksek mekanik, termal dayanım, sıvı dayanımı ve yalıtkanlık özellikleri elde etmek için EPDM kauçuk ile karıştırılırlar. Böylece elyaf takviyeli EPDM kompozitler oluşur. Elyaf- kauçuk karışımları için 2-5-10 PHR elyaf oranları kullanılmıştır. Pişim özellikleri, mekanik özellikler, sıcak hava ve antifiriz yaşlanma özellikleri incelenmiştir.ABSTRACTEPDM is a conventional rubber type, very well known with its good ozone and weather resistance, fair temperature resistance, successful resistance to polar liquids like water and coolant and poor resistance to hydrocarbons. Fibers that are used in the study are carbon, basalt, PA2 glass, PP4 glass and aramid. Carbon fiber is very well known with high tenacity, high modulus of elasticity, high brittleness, low creeping tendency, chemically inert behaviour, low heat expansion and good electrical conductivity. Basalt fiber is capable to withstand very high temperature and can act as fire blocking element. It has good thermal resistance, strength, high friction coefficient and low wear rate. It has superior electrical insulating properties. It has high performance of sea water resistance and UV radiation resistance. Glass fibers have a high tenacity at a low elongation combined with low density. Aramid fibers are a class of heat-resistant and strong synthetic fibers. Fibers are blended with EPDM rubber to have improved characteristics of the components separately in a composite structure like higher mechanical properties, thermal resistance, fluid resistance and insulating properties. Hence fiber filled EPDM composites are held. Firstly 2, 5, 10 PHR fiber ratios are used to be blended inside EPDM rubber mixture Daha fazlası Daha az

Huntit ve hidromanyezit mineralleri içeren alev geciktirici kompozitlerin imalatında amonyum polifosfatın sinerjik etkisinin araştırılması Investigations of the synergstic effect of ammonium polyphosphate ın the manufacture of flame retardant composites containing huntite and hydromagnesite minerals

Kuru, Buket

Yüksek Lisans | 2022 | Fen Bilimleri Enstitüsü

ÖZETBu çalışmada, fosfor-azot bazlı şişen yangın geciktirici sistem ve Türk Huntit/Hidromanyezit mineral kombinasyonundan oluşan alev geciktirici kompozitlerin termal, mekanik ve yanma davranış özellikleri incelendi.Mineral bazlı alev geciktiriciler kullanıldığında kompozitin mekanik performansı gerilediği için fosfor-azot bazlı şişen alev geciktiriciler kullanılarak, alev geciktirici V0 sınıfından ayrılmadan kompozitin mekanik özellikleri iyileştirilmeye çalışıldı. Huntit/hidromanyezit ve fosfor-azot bazlı şişen alev geciktirici katkı karışımları içeren polipropilen bazlı kompozitler, çift vidalı bir ekstrüder kullanılarak ekstrüzy . . .on işleminde hazırlandı. Kompozit karışım yüksek hızlı laboratuvar termokinetik karıştırıcı mikseri kullanılarak eritildi. Plakalar sıcak preslendi, ardından soğuk prese bırakıldı. Mekanik ve yanıcılık testleri için test numuneleri sırasıyla ISO 527-2 standardı, ISO 178 standardı ve UL 94 dikey yanıcılık standartlarına göre hazırlandı.ABSTRACTIn this study, thermal, mechanical and combustion behavior properties of flame retardant composites consisting of phosphorus-nitrogen based intumescent fire retardant system and Turkish Huntite/Hydromagnesite mineral combination were investigated. One of the primary challenges arises from the requirement to achieve good mechanical performance in the composite when using mineral-based flame retardants. For this reason, by using intumescent flame retardants, it has been tried to reduce the mineral ratio in the composite without leaving the flame retardant V0 class.Polypropylene-based composites containing Huntite/hydromagnesite and phosphorus-nitrogen-based intumescent flame retardant mixtures were prepared in the extrusion process using a twin screw extruder. The composite mixture was melted using a high-speed laboratory thermokinetic mixer. The plates were hot pressed, then cold pressed. Test samples for mechanical and flammability tests were prepared according to ISO 527-2 standard, ISO 178 standard and UL 94 vertical flammability standards, respectively Daha fazlası Daha az

Effect of natural fiber wastes on polyolefin and thermoplastic based materialsDoğal elyaf atıkların poliolefin ve termoplastik malzemeler üzerindeki etkisi

Yaşar, Fadıl Anzer

Yüksek Lisans | 2019 | Graduate School of Natural and Applied Sciences

Özet:Küresel çevre sorunları, biyo-temelli malzemelere olan ilginin artmasına neden olmuştur. Yenilenebilir hammaddelere odaklanmak, biyolojik olarak parçalanabilir veya makul bir maliyette geri dönüştürülebilir malzemelerle uğraşmayı sağlayabilir.Çevre dostu malzemelere olan talebin artması ve geleneksel liflerin maliyetini azaltma isteği sonucunda, birçok doğal lif kompoziti geliştirilmiştir.Keten, kenevir, muz,pamuk, hindistan cevizi, sisal ve jüt gibi doğal lifler bilim ve teknoloji ile uğraşan kişilerin tüketim malları, düşük maliyetli konutlar ve diğer sivil yapılardaki uygulamalar için ilgi odağı olmaktadır.Bu çalışmanın amac . . .ı, doğal elyaf atıklarını ve termoplastik proses atıklarını değerlendirmektir.Summary:Global environmental issues have led to a renewed interest in bio-based materials, with the focus on renewable raw materials which can be biodegradable or recyclable at reasonable costs. As a result of the increasing demand for environmentally friendly materials and the desire to reduce the cost of traditional fibers, many natural fiber composites have been developed. Natural fibers like flax, hemp, banana, cotton, coir, sisal, and jute have attracted the attention of scientists and technologists for applications in consumer goods, low-cost housing, and other civil structures. The objective of this study is to evaluate natural fiber waste and thermoplastic process waste Daha fazlası Daha az

6698 sayılı Kişisel Verilerin Korunması Kanunu kapsamında yükümlülüklerimiz ve çerez politikamız hakkında bilgi sahibi olmak için alttaki bağlantıyı kullanabilirsiniz.

creativecommons
Bu site altında yer alan tüm kaynaklar Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır.
Platforms