Joining Aluminum 6061 Alloy Thin Sheets by Friction Stir Spot Welding Method

Serkan GÜNDOĞDU

In this study, the Friction Stir Spot Welding (FSSW) method was employed to join thin AA6061-T4 series aluminum sheets. The AA6061-T4 alloy used in the study has various applications, including aerospace and automotive industries. During the joining process using the FSSW method, emphasis was placed on three parameters: tool rotational speed, pin length, and pin width, considering the advantages of the aluminum alloy used. A total of 12 welding operations were performed with different parameter combinations. The obtained specimens were examined for their mechanical properties, temperature meas ...Daha fazlası

Erişime Açık

Optimization of Nb-Ti-B Master Alloy in Aluminum A356 Parts with General Factorial and Neuro-Regression

Batuhan Doğdu

Al-Si döküm alaşımlarında bir güçlendirme mekanizması olarak uygulanan tane inceltme işlemi, ağırlıklı olarak otomotiv endüstrisinde kullanılan A356 alaşımı söz konusu olduğunda kritik bir öneme sahiptir. Ti-B içeren tane incelticilerin kullanımının neden olduğu solma ve zehirlenme etkilerinin ardından, araştırmacılar yeni bir tane inceltici bileşimi arayışına girmişlerdir. Son yıllarda detaylı olarak çalışılan Nb-B içeren tane inceltici ana alaşımın olumlu etkilerinin görülmesi ancak bu etkilerin kayda değer bir sonuç üretmemesi üzerine Nb-Ti-B üçlü bileşimi üzerinde çalışmalar yapılmı ...Daha fazlası

Erişime Açık

Aging Heat Treatment of Additive Manufacturing Maraging Steels in Nitrogen Containing Atmospheres

Derya Çakan

Additive Manufacturing (AM) is a manufacturing method that pushes the limits of imagination and eliminates the question of whether complex industrial products can be produced that cannot be obtained with traditional manufacturing methods. In this study, microstructure and mechanical properties of maraging steels produced by DMLS method and aged in different durations (6 and 9 hours) and atmospheres (Air, N2 and N2/H2) were investigated. When the SEM images were examined, it was ob-served that the molten pool boundaries did not disappear completely but became blur-red with increasing temperatur ...Daha fazlası

6698 sayılı Kişisel Verilerin Korunması Kanunu kapsamında yükümlülüklerimiz ve çerez politikamız hakkında bilgi sahibi olmak için alttaki bağlantıyı kullanabilirsiniz.

creativecommons
Bu site altında yer alan tüm kaynaklar Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır.
Platforms